Foamed polyester resin

DETAILED DESCRIPTION I claim: 1.
The method of preparing objects of a foamed-filled polyester resin material which comprises (a) preparing a liquid resin blend comprised of a liquid polyester resin, an inorganic filler, bicarbonate of soda, and an effective amount of a cell stabilizing mixture containing sodium acetate, aluminum ammonium sulfate, ferrous ammonium sulfate and tannic acid; (b) preparing a catalyst blend comprised of an effective amount of an organic peroxide catalyst for the polyester resin, an acidic substance effective to release carbon dioxide from the bicarbonate of soda, and water; (c) combining the resin blend and the catalyst blend to form a uniform liquid mixture; and (d) applying that mixture to a mold or surface and allowing the mixture to foam.
2.
The method of claim 1 in which the inorganic filler is a mixture of wollastonite nepheline syenite and mica.
3.
The method of claim 1 in which the sodium bicarbonate is present in an amount equal to 1-3% of the peroxide catalyst weight.
4.
The method of claim 3 in which the acidic substance is glacial acetic acid which is present in an amount sufficient to effect the release of carbon dioxide from the sodium bicarbonate.
5.
The method of claim 4 in which the organic peroxide catalyst is a mixture of benzoyl peroxide and methyl ethyl ketone peroxide in which each is present in an amount equivalent to 0.
5-3.
5% by weight of the polyester resin.
6.
The method of claim 1 in which each of the ingredients is present in an amount equivalent to about 1/2% of the benzoyl peroxide by weight.
7.
The method of claim 6 in which the amount of water present in the catalyst mixture is about 1-4% of the weight of the organic peroxide catalyst and the glacial acetic acid.
8.
The method of claim 7 in which the inorganic filler is present in an amount of up to about 80% by weight of the combined resin-filler mixture.




Description:
BACKGROUND OF THE INVENTION It is generally known that objects made of foamed polyester resins are stronger both in tensile and elongation strength than nonfoamed polyesters