Making silicon carbide bodies

DETAILED DESCRIPTION I claim: 1.
A method of making a reaction-bonded silicon carbide body by steps which include preparing a porous preform comprising compacted particulate silicon carbide and a carbon-yielding binder, heating the preform to convert the binder to carbon and, while the preform in a vacuum or inert atmosphere is in contact with a source of silicon in the form of a compacted silicon cake, made from ingredients including particulate silicon and a carbon-yielding binder, to cause melting and migration into the preform of silicon from the silicon cake, characterised thereby that the silicon cake is made essentially only of silicon metal in flake form and the binder, the amount of binder used in making the silicon cake being at least 10% by weight of the silicon, and the binder, when mixed with the silicon, is in such liquid state that it wets the silicon substantially throughout and provides a coating of binder on surfaces of substantially all the silicon flakes.
2.
A method according to claim 1, characterised thereby that the binder used in the silicon cake is water soluble.
3.
A method according to claim 2, characterised thereby that the binder is sodium lignone sulphonate.
4.
A method according to claim 3, in which the silicon content of the silicon cake is about twice the theoretical amount required for conversion to silicon carbide of the carbon content of the preform.
5.
A method according to claim 2, in which the silicon content of the silicon cake is about twice the theoretical amount required for conversion to silicon carbide of the carbon content of the preform.
6.
A method according to claim 1, in which the silicon content of the silicon cake is about twice the theoretical amount required for conversion to silicon carbide of the carbon content of the preform.




Description:
This invention relates to making silicon carbide bodies and provides an improved method of making reaction-bonded, silicon carbide bodies.
It is known, from Published U.
K.
Patent Application No