Method for preparing improved expanded polystyrene sheet

DETAILED DESCRIPTION I claim: 1.
In a process for producing microcellular expanded styrene polymer sheet by extruding a mixture containing styrene polymer, a blowing agent and a nucleating system, the improvement comprising extruding with said mixture about 0.
002 to 2%, based on the total weight of styrene polymer, of hydrophobic silica, said hydrophobic silica being uniformly distributed throughout said mixture whereby said sheet has improved flexability.
2.
The improved process of claim 1 wherein said hydrophobic silica is blended with the styrene polymer before it is fed into the extruder.
3.
The improved process of claim 1 wherein said hydrophobic silica is added to the styrene polymer in the barrel of the extruder.
4.
The improved process of claim 1 wherein the amount of hydrophobic silica extruded with said mixture is about 0.
01 to 0.
5%, based on the total weight of styrene polymer.
5.
The improved process of claim 1 wherein expandable polystyrene material is used in forming said mixture.
6.
The improved process of claim 1 wherein a portion of the styrene polymer is general purpose polystyrene and a portion of the blowing agent is injected into the molten polymer while it is in the barrel of the extruder.
7.
The improved process of claim 1 wherein the styrene polymer is general purpose polystyrene and the blowing agent is injected into the molten polymer while it is in the barrel of the extruder.
8.
A process of extruding expanded styrene polymer sheet having a small and uniform cell size from styrene polymer feedstock comprising extruding a mixture comprised of the styrene polymer, about 3-10% blowing agent, about 0.
01 to 5% nucleating system, and about 0.
002 to 2% hydrophobic silica having an average particle size of about 1 to 100 millimicrons, said percentages being based on the total weight of styrene polymer being extruded.
9.
The process of claim 8 wherein said blowing agent, nucleating system and hydrophobic silica are present in the amounts of about 5 to 7%, about 0.
05 to 3% and about 0