Process for the production of pressed block fuel elements of high power for gas cooled high temperature reactor

DETAILED DESCRIPTION What is claimed is: 1.
In a process for the production of molded block fuel elements of high power for gas cooled high temperature reactors by premolding in a first step a graphite matrix block with axially running channels, then inserting in a part of these channels coated fuel particles to fill the block, and finally molding in a further step said premolded and filled block to obtain the block fuel element, the improvement comprising providing inner bars and an outer molding die frictionally moveable in the axial direction and a pair of opposed molding punches, moving said punches within said outer die to premold said matrix block in said first step, and to finally mold said filled block in said further step, said bars in said first step moving unhindered relative to said punches in accordance with the frictional forces generated between said bars and the graphite matrix block.
2.
A process according to claim 1 comprising separately premolding the coated particles overcoated with the same graphite-resin powder mixture used for manufacture of whole graphite matrix, and then inserting said premolded overcoated fuel particles in the graphite matrix and completing the molding of the block fuel element under pressure.
3.
A process according to claim 2 wherein the graphite matrix includes a binder resin capable of softening and premolding the matrix at the softening temperature of said binder under low pressure.
4.
In a process for molding nuclear reactor fuel elements having channels therethrough from a granular graphite material comprising: providing a die having an axial bore therethrough; providing a pair of axially spaced apart molding punches in said bore; providing a plurality of axially extending channel-forming bars in said bore, said bars passing loosely through said punches; placing granular graphite material in the bore of said die between said punches and in surrounding relationship to said bars; moving said punches within said bore to mold a fuel element matrix, said bars moving unhindered relative to said punches and in accordance with the frictional forces generated between the graphite material and said bars; and removing the resulting channelled matrix from said die and from said bars