Bonded reinforced plastic structures

DETAILED DESCRIPTION What is claimed is: 1.
A bonded reinforced plastic structure which comprises reinforced plastic parts coated with a primer coat and bonded together by a thermoplastic block copolymer, wherein the reinforced plastic is formed from sheet molding compound or bulk molding compound, wherein the primer coat comprises an epoxidized novolac resin and a resinous amidopolyamine in a weight ratio of about 2:1 to about 1:2, wherein the block copolymer comprises from 40 to 80% by weight of crystalline polyester or polyamide segments and from 20 to 60% by weight of amorphous polyamide or polyether segments, and wherein the block copolymer has a crystalline melting point above about 155.
degree.
C.
and a number average molecular weight in the range of about 8000 to about 30000.
2.
The bonded structure of claim 1 wherein the crystalline segments of the block copolymer are polyethylene terephthalate or polybutylene terephthalate and the amorphous segments comprise a polyamide condensation product of a dimer acid containing 75 to 98 weight percent dimer and an aliphatic primary diamine containing from 2 to 10 carbon atoms.
3.
The bonded structure of claim 1 wherein the epoxidized novolac resin has an epoxy functionality of from 3 to 5 and is the reaction product of epichlorohydrin and a novolac containing from 3 to 6 phenolic hydroxyl groups per molecule and the resinous amidopolyamine is an amine terminated polyamide of amine equivalent weight in the range of about 40 to about 600 prepared by condensation of a C.
sub.
2 to C.
sub.
10 primary polyamine and a fatty dicarboxylic acid containing at least 6 carbon atoms and wherein the primer coating thickness is in the range of about 5 to about 25 microns.
4.
The bonded structure of claim 3 wherein the amine terminated polyamide is a condensate of a C.
sub.
2 to C.
sub.
10 primary polyamine and a dimer acid containing from 75 to 98 weight percent dimer and 25 to 2 weight percent trimer.
5.
The bonded structure of claim 3 wherein the polyamine component of the primer coat comprises up to 70 weight percent of an aromatic C