Process for producing crystal-oriented permanent magnets

DETAILED DESCRIPTION What is claimed is: 1.
In a process for preparing anisotropic permanent magnets, comprising the steps of introducing molten permanent magnet material into a vertically elongated mold, unilaterally abstracting heat to solidify the material in said mold and to cause growth of crystals in an upward direction from the bottom of the mold, removing mold material from the magnet material after solidification of the magnet material into a bar, treating the surface of the solidified bar with an etching solution to expose the crystalline structure of the bar, and subdividing the etched bar.
2.
A process as claimed in claim 1, which includes the step of sandblasting the solidified bar prior to said etching step.
3.
A process as claimed in claim 2, which includes the step of cleaning said solidified bar prior to said sandblasting step.
4.
A process as claimed in claim 1, wherein the etching solution is comprised of: (a) 7 to 20 percent by weight of sulfuric acid; (b) 2 to 8 percent by weight of hydrochloric aicd; (c) 0.
3 to 1.
5 percent by weight of hydrogen peroxide; (d) 0.
05 to 1 percent by weight of ferric chloride; (e) 0.
01 to 0.
2 percent by weight of cupric chloride; and the remainder water.
5.
A process as claimed in claim 1, wherein the etching solution is comprised of: (a) about 14.
4 percent by weight of sulfuric acid; (b) about 4.
1 percent by weight of hydrochloric acid; (c) about 0.
78 percent by weight of hydrogen peroxide; (d) about 0.
22 percent by weight of ferric chloride; (e) about 0.
043 percent by weight of cupric chloride; and (f) the remainder water.
6.
A process as claimed in claim 5, which includes the step of sandblasting said solidified bar prior to said etching step, and said etching step includes immersing said bar in said solution for a period of time between 7 and 14 minutes.
7.
A process as claimed in claim 6, which includes the step of removing said etching solution by the application of water.
8.
A process as claimed in claim 1, wherein the permanent magnetic material comprises an aluminum-nickel-cobalt-iron alloy, a samarium-cobalt alloy or an alloy of rare earths and cobalt