Method for producing a strontium metal film on internal surfaces of a CRT

DETAILED DESCRIPTION I claim: 1.
A method for producing within an evacuated electron tube a strontium metal film for sorbing residual gases comprising positioning within said envelope a mass comprising an alloy consisting essentially of about 40 weight parts strontium metal and about 55 to 65 weight parts aluminum metal, sealing said envelope, heating said mass until a substantial proportion of the strontium in said mass is liberated and vaporized, and condensing said vaporized strontium as a metal film on surfaces within said envelope.
2.
The method defined in claim 1 wherein said mass consists essentially of 0 to 60 weight parts nickel metal particles and about 43 weight parts particles of said alloy.
3.
The method defined in claim 2 wherein said mass consists essentially of about 53 to 60 weight parts nickel metal particles and about 43 weight parts particles of said alloy.
4.
The method defined in claim 1 wherein said mass includes a material which releases gas at temperatures below the temperatures at which said strontium is liberated and vaporized from said mass.
5.
The method defined in claim 4 wherein said gas-releasing material is at least one member of the group consisting of iron nitride, nickel nitride, germanium nitride, barium nitride, phosphorus nitride, titanium hydride and barium hydride.
6.
The method defined in claim 4 wherein said gas-releasing material is iron nitride.
7.
A method for reducing X-radiation generated within a cathode-ray tube, said tube comprising an evacuated envelope, a luminescent viewing screen within said envelope, means for producing a plurality of electron beams within said envelope for exciting said screen to luminescence, and an apertured mask closely spaced from said screen for intercepting and transmitting selected portions of said beams, said method comprising a positioning within said envelope a compressed mass consisting essentially of strontium-aluminum alloy particles and nickel metal particles, said alloy consisting essentially of about 40 weight parts strontium metal and about 55 to 65 weight parts aluminum metal, b sealing said envelope, c heating said mass until said mixture flashes by exothermic reaction and a substantial proportion of the strontium therein is released as strontium metal vapor, d and condensing vaporized strontium metal on internal surfaces of said envelope and at least a substantial portion of the electron-beam receiving surface of said mask