Method of controlling filament formation in a glass fiber bushing

DETAILED DESCRIPTION We claim: 1.
A method of controlling the formation of filaments from a molten glass source in a fiber forming bushing comprising establishing in the bushing at least two groups of orifices, the orifices in each of the groups having different diameters, pulling glass fibers from each group of orifices simultaneously and chopping the fibers into discrete lengths as they are being pulled, and controlling the formation and pulling of the glass fibers to minimize interruption by maintaining the difference in orifice size in any two groups between 0.
0215 to 0.
015 inch.
2.
The method of claim 1 where the differences in the orifice diameter are controlled between 0.
021 to 0.
018 inch.
3.
The method of claim 1 wherein one group of orifice is maintained at diameter of 0.
067 inch and a second group of orifices is maintained at 0.
048 inch.
4.
A method of controlling the formation of filaments from a fiber forming bushing comprising continuously pulling glass fibers from a bushing from at least two groups of orifices, each group of orifices being controlled to provide orifices of the same size in each group, controlling the diameter of the orifices in one group to maintain the orifices at a diameter different than the other group while controlling the magnitude of the difference between 0.
0215 to 0.
015 inch, and collecting the filaments formed from each group of orifices at the same pulling speed.
5.
The method of claim 4 wherein the orifices of one group are 0.
067 inch in diameter and the orifices of a second group are at 0.
048 inch.
6.
The method of claim 4 wherein the difference in diameter of the groups of orifices is maintained between 0.
021 inch and 0.
018 inch.




Description:
BACKGROUND OF THE INVENTION In the manufacture of glass fibers a molten glass is typically drawn from a precious metal container called a bushing in the art through a plurality of orifices located in the bottom of the container.
The container is electrically heated to maintain the glass in it in the molten state